Methods for removing hemicellulose

ABSTRACT

A method for treating a cellulosic material comprises extracting the cellulosic material with an extractant to selectively extract hemicellulose therein and separating the extracted hemicellulose to form a cellulosic product comprising less hemicellulose than the cellulose-containing material. The extractant comprises an ionic liquid and a non-solvent. The cellulosic product retains the cellulosic fiber morphology.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a divisional of U.S. application Ser. No. 13/827,881, filed Mar. 14, 2013, which claims priority to U.S. Provisional Application 61/684,993, filed Aug. 20, 2012, the entireties of which are incorporated herein by reference.

FIELD OF THE INVENTION

The present invention relates generally to the removal of hemicellulose from cellulose containing materials. In particular, the present invention relates to methods for extracting hemicellulose from cellulose containing materials.

BACKGROUND OF THE INVENTION

Cellulose is typically obtained from wood pulp and cotton and may be further modified to create other derivatives including cellulose ethers, cellulose esters and cellulose nitrate, among others. Cellulose derivatives have a variety of commercial uses. For example, cellulose acetate is the acetate ester of cellulose and is used for a variety of products, including textiles (e.g., linings, blouses, dresses, wedding and party attire, home furnishings, draperies, upholstery and slip covers), industrial uses (e.g., cigarette and other filters for tobacco products, and ink reservoirs for fiber tip pens, decking lumber), high absorbency products (e.g., diapers, sanitary napkins, and surgical products), thermoplastic products (e.g., film applications, plastic instruments, and tape), cosmetic and pharmaceutical (extended capsule/tablet release agents and encapsulating agent), medicinal (hypoallergenic surgical products) and others.

High purity α-cellulose is required as a starting material to make cellulose derivatives, such as cellulose acetate. Acetate-grade pulps are specialty raw materials produced in commercial pulp processes, but the cost for such pulps is high. Commercial paper grade pulps contain less than 90% α-cellulose and are potential crude cellulosic sources for making cellulose derivatives. However, paper grade pulp also contains a high amount of impurities, such as hemicellulose, rendering it incompatible with certain industrial uses, such as making acetate flake or tow.

Zhou et al. discusses the use of dimethyldioxirane (DMDO), a pulp bleaching agent, to treat birch pulp and obtain acetate-grade pulp. However, DMDO is not commercially available due to its instability. Therefore, it is not an ideal solvent for producing large quantities of high α-cellulose pulp. Zhou et al. “Acetate-grade pulp from birch,” BioResources, (2010), 5(3), 1779-1778.

Studies have been done regarding the treatment of biomass to form biofuels. Specifically, it is known that various ionic liquids can be used to dissolve cellulosic material. S. Zhu et al. in Green Chem. 2006, 8, pp. 325-327, describe the possibility of dissolving cellulose in ionic liquids and recovering it by addition of suitable precipitates such as water, ethanol, or acetone.

Others have used ionic liquids to break down the cellulosic materials to make biofuels by way of glucose. For example, US Pat. Appl. 2010/0112646 discloses a process for preparing glucose from a cellulose material, in which a cellulose-comprising starting material is provided and treated with a liquid treatment medium comprising an ionic liquid and an enzyme. Similarly, US Pat. Appl. 2010/0081798 discloses a process for preparing glucose from a material containing ligno-cellulose, in which the material is first treated with an ionic liquid and then subjected to enzymatic hydrolysis. US Pat. Appl. 2010/0081798 describes obtaining glucose by treating a material containing lingo-cellulose with an ionic liquid and subjecting same to an enzymatic hydrolysis and fermentation. However, in order to turn cellulose containing materials into glucose, the methods disclosed in these references result in breaking down the cellulose molecules, making them unsuitable for use as starting materials to make cellulose derivatives.

U.S. Pat. No. 7,828,936 describes a method for dissolving cellulose in which the cellulose based raw material is admixed with a mixture of a dipolar aprotic intercrystalline swelling agent and an ionic liquid. This method results in the complete dissolution of the cellulose and destruction of the fiber morphology of the cellulose. Although the cellulose may be regenerated using a non-solvent, the crystallinity of the regenerated cellulose is lower than the original cellulose sample.

Therefore the need exists for methods for producing high purity α-cellulose from lower grade starting materials without destroying the fiber morphology and other characteristics of the cellulose structure. In particular, the need exists for cost effective methods for removing hemicellulose from cellulosic materials to recover high purity α-cellulose that can be converted to other cellulose derivatives.

SUMMARY OF THE INVENTION

In a first embodiment, the present invention is directed to a method for treating a cellulosic material. The method comprises the step of extracting the cellulosic material with an extractant to selectively extract hemicellulose. Preferably, the extractant comprises an ionic liquid and a non-solvent. The non-solvent preferably is capable of precipitating the cellulosic product. In an embodiment, the non-solvent is water, DMSO, or a combination thereof. The method further comprises the step of separating the extracted hemicellulose from a cellulosic product, which comprises less hemicellulose than the cellulosic material. Preferably, the cellulosic product comprises at least 20% less hemicellulose than the cellulosic material. Preferably, the cellulosic product retains a cellulosic fiber morphology. In another embodiment, the cellulosic product retains other suitable characteristics such as intrinsic viscosity and brightness.

In a second embodiment, the present invention is directed to a method for producing high purity α-cellulose grade pulp. The method comprises the step of extracting hemicellulose from a wood pulp by treating the wood pulp with an extractant comprising an ionic liquid and a non-solvent to form an intermediate wood pulp that retains a cellulosic fiber morphology and other suitable characteristics such as intrinsic viscosity and brightness. The method further comprises treating the intermediate wood pulp with an enzyme to hydrolyze hemicellulose contained therein and forming a reduced hemicellulose wood pulp. The method further comprises the step of washing the reduced hemicellulose wood pulp with a wash solution to form the high purity α-cellulose grade pulp. In an embodiment, the wash solution is selected from the group consisting of DMSO, N-methyl pyrrolidone, DMF, methanol, ethanol, isopropanol, dimethyl carbonate, acetone and/or water.

In a third embodiment, the present invention is directed to a high purity α-cellulose grade pulp product purified by removing hemicellulose from cellulosic material using a mixture of ionic liquid, water and enzyme. The high purity α-cellulose grade pulp product comprises less than 5% hemicellulose.

In a fourth embodiment, the present invention is directed to a solvent system for selectively reducing hemicellulose in a cellulosic material to form a hemicellulose reduced cellulosic product. Preferably, the solvent system comprises 50-80 wt. % ionic liquid and 20-50 wt. % water. In one embodiment, the solvent system further comprises DMSO, DMF, methanol, ethanol, isopropanol, acetone, acetic acid or a mixture thereof.

In a fifth embodiment, the present invention is directed to a solvent system for selectively reducing hemicellulose in a cellulosic material to form a hemicellulose reduced cellulosic product. Preferably, the solvent comprises 0.1-7.9 wt. % ionic liquid and 92.1-99.9 wt. % DMSO.

In a sixth embodiment, the present invention is directed to a solvent system for selectively reducing hemicellulose in a cellulosic material to form a hemicellulose reduced cellulosic product. Preferably, the solvent comprises at most 50 wt. % ionic liquid, at most 18 wt. % water, and at least 50 wt. % DMSO.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will be better understood in view of the appended non-limiting figures, in which:

FIG. 1 shows the structure and morphology of a pre-treated hardwood paper grade pulp.

FIG. 2 shows the structure and morphology of a pre-treated softwood paper grade pulp.

FIG. 3 shows the structure and morphology of a reduced hemicellulose cellulosic product obtained using the inventive method to treat a hardwood paper grade pulp.

FIG. 4 shows the structure and morphology of a reduced hemicellulose cellulosic product obtained using the inventive method to treat a softwood paper grade pulp.

FIG. 5 shows the structure and morphology of a hardwood paper grade pulp treated with an ionic liquid and reconstituted using a non-solvent.

FIG. 6 shows the structure and morphology of a softwood paper grade pulp treated with an ionic liquid and reconstituted using a non-solvent.

DETAILED DESCRIPTION OF THE INVENTION Introduction

The methods of the present invention are suitable for removing impurities, such as hemicellulose, from a cellulosic material. Generally speaking, the term “cellulosic material” includes cellulose and hemicellulose. The process of the invention generally includes the step of selectively extracting hemicellulose with an extractant. Preferably, the extractant includes an ionic liquid and a non-solvent. The extracted hemicellulose is then separated from the cellulosic product. As a result, the cellulosic product comprises less hemicellulose than the starting cellulosic material, e.g., at least 10% less, at least 20% less or at least 30% less hemicellulose than the starting cellulosic material.

In one embodiment, the cellulosic material may be subjected to one more extraction steps with the extractant. The extractant includes an ionic liquid that is suitable for extracting hemicellulose from the cellulosic material. The use of an ionic liquid alone may dissolve both hemicellulose and α-cellulose thereby destroying the fiber morphology of the cellulosic material and increasing the degree of difficulty for separation and recovery of the cellulosic products. Once destroyed, the original fiber morphology of the cellulosic material disappears and cannot be regenerated. It has now been discovered that by using a mixture of ionic liquid and non-solvent at appropriate proportions, hemicellulose may be selectively extracted without destroying significant amounts of the cellulosic fiber morphology. Therefore, the fiber morphology of the cellulosic material is retained in the cellulosic product. Without being bound by theory, α-cellulose is generally insoluble in the ionic liquid/non-solvent extractant, while hemicellulose is soluble therein. As used herein, the term “non-solvent” refers to liquids that are capable of reducing α-cellulose solubility in the selected ionic liquid to a point that the α-cellulose does not readily dissolve in a mixture of the non-solvent and the ionic liquid. Therefore, the non-solvent in combination with the ionic liquid selectively dissolves the hemicellulose but leaves the cellulose substantially intact. In addition, other characteristics of the cellulosic material are also retained, such as intrinsic viscosity and brightness. Thus, the resulting cellulosic product has a reduced amount of hemicellulose, but retains the fiber morphology, intrinsic viscosity and brightness of the cellulosic material. In one embodiment, less than 15% of the cellulose in the cellulosic material is extracted, e.g., less than 10%, or less than 5%, as determined by HPLC based carbohydrate analysis. In one embodiment, the cellulosic material may be subjected to repeated extraction steps with the extractant.

In one embodiment, the cellulosic material may also be treated with an enzyme to hydrolyze the hemicellulose to form a reduced hemicellulose product. It has now been discovered that by treating cellulosic materials with both the extractant and an enzyme, a substantially hemicellulose-free cellulosic product may be recovered. For example, the cellulosic product may comprise less than 5% hemicellulose, less than 3% hemicellulose, or less than 2% hemicellulose. Surprisingly and unexpectedly, the order of extractant and enzyme treatments of the cellulosic material affects the amount of hemicellulose removed from the cellulosic material. In preferred embodiments, the cellulosic material is treated with the extractant prior to enzyme treatment (although the reverse sequence of steps is also contemplated). In one embodiment, the cellulosic material may be treated with the extractant again after the enzyme treatment, optionally followed by another enzyme treatment step. The extractant and enzyme treatment steps may be further repeated as desired to obtain the desired α-cellulose purity.

In one embodiment, the non-solvent may be an organic solvent or an aqueous solvent. In one embodiment, the non-solvent may be selected from water, dimethylformamide (DMF), dimethyl sulfoxide (DMSO), methanol, ethanol, isopropanol, acetone, acetic acid, and mixtures thereof.

In one embodiment, solvents may be used to wash and remove the ionic liquid from the cellulosic product. For example, DMSO, DMF, methanol, ethanol, isopropanol, acetone, dimethyl carbonate or mixtures thereof may be used as a washing agent for the cellulosic material.

In another embodiment, acetone and/or water may be used as a rinsing agent to remove other solvents from the reduced hemicellulose product before drying to produce the final cellulosic product.

Process for Removing Hemicellulose

The present invention is broadly applicable to the treatment of natural cellulose-containing materials, including plant and plant-derived materials. As used herein, the term “cellulose-containing material” includes, without limitation, plant derived biomass, corn stover, sugar cane bagasse and cane residues, rice and wheat straw, agricultural grasses, woodchips, and other forms of wood, bamboo, and all other materials proximately or ultimately derived from plants.

Generally, cellulosic material may be derived from lignin-containing materials, where lignin has been removed therefrom. In cellulosic materials, hemicellulose is linked to cellulose by hydrogen bonds. Overall, the cellulosic material has a linear shape of fiber morphology, which is surrounded by hemicellulose via hydrogen bonds. These bonds between cellulose and hemicellulose may become weakened by treating the cellulosic material with an extractant to selectively dissolve the hemicellulose while maintaining the fiber morphology of the cellulosic material.

The cellulosic material may be provided as pellets, sheets or chips. Exemplary sources of cellulosic material include, but are not limited to, rice straw, hard wood, hardwood pulp, soft wood, softwood pulp, herbs, recycled paper, waste paper, wood chips, pulp and paper wastes, waste wood, thinned wood, cornstalk, chaff, wheat straw, sugar cane stalk, bagasse, agricultural residual products, agricultural wastes, excretions of livestock, or mixtures thereof. In an embodiment of the invention, the cellulosic material is a paper grade pulp provided in forms such as, but not limited to, rolls, sheets, or bales. Preferably, the paper grade pulp comprises at least 70 wt. % α-cellulose, e.g., at least 80 wt. % α-cellulose or at least 85 wt. % α-cellulose. Paper grade pulp typically also comprises at least 5 wt. % hemicellulose, at least 10 wt. % hemicellulose or at least 15 wt. % hemicellulose. In another embodiment, the cellulosic material may be other α-cellulose containing pulps, such as viscose grade pulp, rayon grade pulp, semi-bleached pulp, unbleached pulp, bleach pulp, Kraft pulp, absorbent pulp, dissolving, or fluff. These cellulosic materials may be treated using the inventive method to produce high purity α-cellulosic products.

Cellulose is a straight chain polymer and is derived from D-glucose units, which condense through β-1,4-glycosidic bonds. This linkage motif contrasts with that for α-1,4-glycosidic bonds present in starch, glycogen, and other carbohydrates. Unlike starch, there is no coiling or branching in cellulose and cellulose adopts an extended and rather stiff rod-like confirmation, which is aided by the equatorial confirmation of the glucose residues. The multiple hydroxyl groups on the glucose from one chain form hydrogen bonds with oxygen atoms on the same or on a neighboring chain, holding the chains firmly together side-by-side and forming microfibrils with high tensile strength, which then overlay to form the macrostructure of a cellulose fiber. In an embodiment of the invention, the cellulosic product retains the fiber structure after the extraction of hemicellulose.

Hemicellulose is a polysaccharide that is typically present along with cellulose in almost all plant cell walls. Hemicellulose can be any one of xylan, glucuronoxylan, arabinoxylan, glucomannan, galactomannan, and xyloglucan. These polysaccharides contain many different sugar monomers and can be hydrolyzed.

The process of the present invention is particularly beneficial in that it has shown to be effective for use with paper grade wood pulp that is derived from softwoods and hardwoods. The method of the present invention provides a potential technique for upgrading paper grade pulp produced from softwood species, which are generally more abundant, and faster growing, than most hardwood species.

Softwood is a generic term typically used in reference to wood from conifers (i.e., needle-bearing trees from the order Pinales). Softwood-producing trees include pine, spruce, cedar, fir, larch, douglas-fir, hemlock, cypress, redwood and yew. Conversely, the term hardwood is typically used in reference to wood from broad-leaved or angiosperm trees. The terms “softwood” and “hardwood” do not necessarily describe the actual hardness of the wood. While, on average, hardwood is of higher density and hardness than softwood, there is considerable variation in actual wood hardness in both groups, and some softwood trees can actually produce wood that is harder than wood from hardwood trees. One feature separating hardwoods from softwoods is the presence of pores, or vessels, in hardwood trees, which are absent in softwood trees. On a microscopic level, softwood contains two types of cells, longitudinal wood fibers (or tracheids) and transverse ray cells. In softwood, water transport within the tree is via the tracheids rather than the pores of hardwoods.

Extractant

The extractant for extracting hemicellulose from the cellulosic material may be any extractant capable of dissolving at least 50% of the hemicellulose, preferably at least 75% or at least 90% of the hemicellulose, in the cellulosic material. The extractant should not over-degrade the cellulose. For example, in one embodiment, the extractant dissolves less than 15% of the α-cellulose in the cellulosic material, e.g., less than 10%, or less than 5%.

In accordance to the present invention, the extractant comprises two or more components. According to the invention, the extractant comprises at least an ionic liquid and a non-solvent. In one embodiment, the extractant further includes a second non-solvent. The ionic liquid is preferably capable of penetrating the cellulosic material. As discussed above, the ionic liquid is capable of dissolving both α-cellulose and hemicellulose. The non-solvent as used in accordance with the present invention reduces α-cellulose solubility the in ionic liquid to a point that the α-cellulose does not readily dissolve in a mixture of the non-solvent with the ionic liquid. Preferably, the α-cellulose is insoluble in the non-solvent. The extractant in accordance with the present invention, therefore, has the property of selectively dissolving the hemicellulose that is in the cellulosic material.

Without being bound by theory, the insolubility of the α-cellulose in the non-solvent and the extraction agent maintains the cellulose fiber morphology, while the extractant penetrates the cellulosic material and dissolves and extracts the hemicellulose from the cellulosic material. Depending on the specific non-solvent used in the extractant, the weight percentage of the ionic liquid and the non-solvent in the extractant may vary widely. The extractant may comprise of an ionic liquid and one or more non-solvents. Depending on the non-solvent used in the extractant, the weight percentage of the ionic liquid may also vary.

In one embodiment, the extractant may comprise at least 0.1 wt. % ionic liquid, e.g., at least 1 wt. % or at least 2 wt. %. In terms of upper limits, the extractant may comprise at most 95 wt. % ionic liquid, e.g., at most 90 wt. %, or at most 85 wt. %. In terms of ranges, the extractant may comprise from 0.1 wt. % to 95 wt. % ionic liquid, e.g., from 1 wt. % to 90 wt. %, or from 2 wt. % to 85 wt. %. The extractant may comprise at least 5 wt. % non-solvent, e.g., at least 10 wt. %, at least 15 wt. %, or at least 20 wt. %. In terms of upper limits, the extractant optionally comprises at most 90 wt. % non-solvent, at most 95 wt. %, or at most 99.9 wt. %. In terms of ranges, the extractant optionally comprises from 5 wt. % to 90 wt. % non-solvent, e.g., from 10 wt. % to 95 wt. %, or from 2 wt. % to 99.9 wt. %.

In one embodiment, when the extractant comprises an aqueous non-solvent, the extractant comprises at least 50 wt. % ionic liquid, e.g., at least 65 wt. % or at least 80 wt. %. In terms of upper limits, the extractant may comprise at most 95 wt. % ionic liquid, e.g., at most 90 wt. %, or at most 85 wt. %. In terms of ranges, the extractant may comprise from 50 wt. % to 95 wt. % ionic liquid, e.g., from 65 wt. % to 90 wt. %, or from 70 wt. % to 85 wt. %. The extractant may comprise at least 5 wt. % aqueous non-solvent, e.g., at least 10 wt. %, at least 15 wt. %, or at least 20 wt. %. In terms of upper limits, the extractant may comprise at most 50 wt. % aqueous non-solvent, at most 35 wt. %, or at most 20 wt. %. In terms of ranges, the extractant may comprise from 5 wt. % to 50 wt. % aqueous non-solvent, e.g., from 10 wt. % to 35 wt. %, or from 15 wt. % to 20 wt. %. In one embodiment, the aqueous non-solvent is water.

In one embodiment, when the extractant comprises an organic non-solvent, the extractant comprises at least 0.1 wt. % ionic liquid, e.g., at least 1 wt. % or at least 2 wt. %. In terms of upper limits, the extractant may comprise at most 7.9 wt. % ionic liquid, e.g., at most 7.5 wt. %, or at most 7 wt. %. In terms of ranges, the extractant may comprise from 0.1 wt. % to 7.9 wt. % ionic liquid, e.g., from 1 wt. % to 7.5 wt. %, or from 2 wt. % to 7 wt. %. The extractant may comprise at least 92.1 wt. % organic non-solvent, e.g., at least 93 wt. %, or at least 95 wt. %. In terms of upper limits, the extractant may comprise at most 99.9 wt. % organic non-solvent, at most 98 wt. %, or at most 97 wt. %. In terms of ranges, the extractant may comprise from 92.1 wt. % to 99.9 wt. % organic non-solvent, e.g., from 93 wt. % to 98 wt. %, or from 95 wt. % to 97 wt. %. In one embodiment, the organic non-solvent is DMSO.

In one embodiment, the extractant includes an ionic liquid, a first non-solvent and a second non-solvent. In one embodiment, the extractant includes an equal amount of the second non-solvent as the combination of the ionic liquid and the first non-solvent, i.e., the extractant includes 50 wt. % of the second non-solvent and 50 wt. % of the ionic liquid and the first non-solvent. In one embodiment, the extractant includes from 10 wt. % to 98 wt. % of the second non-solvent, e.g., from 30 wt. % to 90 wt. %, or from 50 wt. % to 80 wt. %. In terms of lower limits, the extractant optionally includes at least 10 wt. % of the second non-solvent, e.g., at least 30 wt. %, or at least 50 wt. %. In terms of upper limits, the extractant optionally includes at most 98 wt. % of the second non-solvent, e.g., at most 90 wt. %, or at most 80 wt. %. Since ionic liquids are generally more expensive to produce than non-solvents, the use of a large amount of the second non-solvent beneficially reduces the cost of purifying the cellulosic material.

In one embodiment, the extractant includes an ionic liquid, an aqueous non-solvent and an organic non-solvent. In one embodiment, the first non-solvent is an aqueous non-solvent and the second non-solvent is an organic non-solvent.

In the tertiary extractant system, the extractant may include at most 50 wt. % ionic liquid, e.g., at most 40 wt. %, or at most 30 wt. %. In terms of lower limit, the extractant may include at least 0.1 wt. % ionic liquid, e.g., at least 5 wt. % or at least 10 wt. %. In terms of ranges, the extractant may include from 0.1 wt. % to 50 wt. % ionic liquid, e.g., from 0.3 wt. % to 40 wt. %, or from 0.5 wt. % to 30 wt. %. In some embodiments, the extractant may include at most 18 wt. % the first non-solvent, i.e., at most 16 wt. %, or 10 wt. %. In terms of ranges the extractant may include from 0.5 wt. % to 18 wt. % the first non-solvent, e.g., from 3 wt. % to 16 wt. % or from 5 wt. % to 8 wt. %. In one embodiment, water is the first non-solvent. DMSO is the second non-solvent. Without being bound by theory, it is postulated that the decrease in viscosity in the extractant by using the second non-solvent beneficially increases the amount of hemicellulose extracted from the cellulosic material.

Ionic Liquid

Ionic liquids are organic salts with low melting points (up to 100° C.), many of which are consequently liquid at room temperature. Specific features that make ionic liquids suitable for use in the present invention include lack of vapor pressure, ability to dissolve a wide range of organic compounds and versatility of chemical and physical properties. In addition, ionic liquids are non-flammable, which makes them suitable for use in the industrial applications.

It has been found that, in addition to these beneficial properties, when contacted with cellulosic materials, including plant matter and plant matter derivatives, the ionic liquids are capable of dissolving the hemicellulose and cellulose contained therein. In addition, with the appropriate choice of treatment conditions (for example, time of contact, temperature, and non-solvent composition), ionic liquids penetrate the structure of the cellulose-containing material to break down the material and extract organic species contained therein. α-Cellulosic components remaining in the cellulosic material are preserved and the fiber morphology is retained.

The ionic liquids refer to liquids consisting of ions only. Ionic liquids existing in a liquid phase at room temperature are called room temperature ionic liquids. Generally, ionic liquids are formed of large-sized cations and a smaller-sized anion. Cations of the ionic liquids may contain nitrogen, phosphorous, sulfur, or carbon. Because of the disparity in size between the cation and anion, the lattice energy of the compound is decreased resulting in a less crystalline structure with a low melting point.

Exemplary ionic liquids include the compounds expressed by the following Formula (1):

[A]⁺[B]⁻  (1)

In one embodiment, the ionic liquid is selected from the group consisting of substituted or unsubstituted imidazolium salts, pyridinium salts, ammonium salts, triazolium salts, pyrazolium salt, pyrrolidinium salt, piperidium salt, and phosphonium salts. In preferred embodiments, [A]⁺ is selected from the group consisting of

wherein R, R¹, R², R³ and R⁴ are each independently selected from the group consisting of hydrogen, C₁-C₁₅ alkyls, and C₂-C₂₀ alkenes, and the alkyl or alkene may be substituted by a substituent selected from the group consisting of sulfone, sulfoxide, thioester, ether, amide, hydroxyl and amine.

[B]⁻ is preferably selected from the group consisting of Cl⁻, Br⁻, I⁻, OH⁻, NO₃ ⁻SO₄ ²—, CF₃CO₂ ⁻, CF₃SO₃ ⁻, BF₄ ⁻, PF₆ ⁻, CH₃COO⁻, (CF₄SO₂)₂N⁻, and AlCl₄ ⁻.

Examples of the ionic liquid may include 1-butyl-3-methyl imidazolium tetrachloroaluminate, 1-ethyl-3-methyl imidazolium tetrachloroaluminate, 1-ethyl-3-methyl imidalzolium hydrogensulfate, 1-butyl-3-methyl imidazolium hydrogensulfate, methylimidazolium chloride, 1-ethyl-3-methyl imidazolium acetate, 1-butyl-3-methyl imidazolium acetate, tris-2(hydroxyl ethyl)methylammonium methylsulfate, 1-ethyl-3-methyl imidazolium ethylsulfate, 1-ethyl-3-methyl imidazolium methanesulfonate, methyl-tri-n-butylammonium methylsulfate, 1-butyl-3-methyl imidazolium chloride, 1-ethyl-3-methyl imidasolium chloride, 1-ethyl-3-methyl imidazolium thiocyanate, 1-butyl-3-methyl imidazolium thiocyanate, 1-aryl-3-methyl imidazolium chloride, and mixtures or complexes thereof, but the disclosed concept of utilizing ionic liquids is not limited to the disclosed species.

The ionic liquid may be commercially available, and may include Basionic™ AC 01, Basionic™ AC 09, Basionic™ AC 25, Basionic™ AC 28, Basionic™ AC 75, Basionic™ BC 01, Basionic™ BC 02, Basionic™ FS 01, Basionic™ LQ 01, Basionic™ ST 35, Basionic™ ST 62, Basionic™ ST 70, Basionic™ ST 80, Basionic™ VS 01, and Basionic™ VS 02, but the disclosed species is not limited thereto.

Alternatively, the compound may be 1-ethyl-3-methyl imidazolium acetate of the following structural formula (2), 1-ethyl-3-methyl imidazolium hydrogensulfate of the following structural formula (3), 1-ethyl-3-methyl imidazolium chloride of the following structural formula (4), or 1-n-butyl-3-methyl imidazolium chloride of the following structural formula (5):

Non-Solvent

As stated above, non-solvents in the context of this invention include solvents that do not have the ability to readily dissolve α-cellulose. In exemplary embodiments, the non-solvent is selected from the group consisting of water, alcohols such as methanol, ethanol, n-propanol, isopropanol, n-butanol, tert-butanol, diols and polyols such as ethanediol and propanediol, amino alcohols such as ethanolamine, diethanolamine and triethanolamine, aromatic solvents, e.g. benzene, toluene, ethylbenzene or xylenes, halogenated solvents, e.g. dichloromethane, chloroform, carbon tetrachloride, dichloroethane or chlorobenzene, aliphatic solvents, e.g. pentane, hexane, heptane, octane, ligroin, petroleum ether, cyclohexane and decalin, ethers, e.g. tetrahydrofuran, diethyl ether, methyl tert-butyl ether and diethylene glycol monomethyl ether, ketones such as acetone and methyl ethyl ketone, esters, e.g. ethyl acetate, dimethyl carbonate, dipropyl carbonate, propylene carbonate, amides, e.g., formamide, dimethylformamide (DMF), dimethylacetamide, dimethyl sulfoxide (DMSO), acetonitrile and mixtures thereof.

In one embodiment, a second non-solvent may be used in conjunction with the first non-solvent and the ionic liquid as described above. In one embodiment, the second non-solvent decreases the viscosity of the extractant. In one embodiment, the second non-solvent has a viscosity of less than 2.0 mPa·s at 25° C. In one embodiment, the second non-solvent is selected from the group consisting of formamide, dimethylformamide (DMF), dimethylacetamide, dimethyl sulfoxide (DMSO), N-methylpyrrolidone, propylene carbonate, acetonitrile and mixtures thereof. It is postulated that using a low viscosity second non-solvent in the extractant, a smaller amount of ionic liquid is needed to extract the hemicellulose in the cellulosic material.

Washing Agent

In one embodiment, the cellulosic product is washed using a washing agent after the hemicellulose is extracted therefrom in the extractant. The primary purpose of the washing step is to remove residual extractant from the cellulosic product as well as remove loosely bound hemicellulose contained therein. The washing agent preferably comprises a non-solvent, which cleanses the cellulose product, but may also include some low level of extractant resulting from the sequence of washing steps. In one embodiment, the washing agent is selected from the group consisting of water, alcohols, polyols, amino alcohols, aromatic solvents, halogenated solvents, aliphatic solvents, ethers, ketones, esters, formamide, dimethylformamide (DMF), dimethylacetamide, propylene carbonate, dimethyl sulfoxide (DMSO), acetonitrile and mixtures thereof. In one embodiment, the washing agent is selected from the group consisting of DMSO, DMF, N-methyl pyrrolidone, methanol, ethanol, isopropanol, dimethyl carbonate, propylene carbonate, acetone, water, and mixtures thereof.

Enzyme

As discussed above, in one embodiment, the cellulosic material is treated with an enzyme, preferably a hemicellulase, to break down residual hemicellulose contained in the cellulosic material. The hemicellulase includes one or more enzymes that hydrolyze hemicellulose to form simpler sugars, ultimately yielding monosaccharides (e.g., glucose, other hexoses, pentoses). Suitable hemicellulase include one or more of xyloglucanase, β-xylosidase, endoxylanase, α-L-arabinofuranosidase, α-glucuronidase, mannanase, and acetyl xylan esterase. Preferably, the enzymes include a combination of both endo-enzymes (i.e., enzymes hydrolyzing internal polysaccharide bonds to form smaller poly- and oligosaccharides) and exo-enzymes (i.e., enzymes hydrolyzing terminal and/or near-terminal polysaccharide bonds) to facilitate the rapid hydrolysis of large polysaccharide molecules. Suitable commercial hemicellulase include SHEARZYME (available from Novozymes A/S, Bagsvaerd, Denmark), PULPZYME (available from Novozymes A/S, Bagsvaerd, Denmark), FRIMASE B210 (available from Puratos, Groot-Bijgaarden, Belgium), FRIMASE B218 (available from Puratos, Groot-Bijgaarden, Belgium), GRINDAMYL (available from Danisco, Copenhagen, Denmark), ECOPULP TX200A (available from AB Enzymes, Darmstadt, Germany), MULTIFECT Xylanase (available from Genencor/Danisco, Palo Alto, USA), PENTOPAN Mono BG (available from Novozymes, Bagsvaerd, Denmark), and PENTOPAN 500 BG (available from Novozymes, Bagsvaerd, Denmark).

The enzymes generally can be used in amounts that are not particularly limited. For example, hemicellulase can be used in amounts ranging from about 0.001 mg/g to about 500 mg/g (e.g., about 0.05 mg/g to about 200 mg/g, about 0.1 mg/g to about 100 mg/g, about 0.2 mg/g to about 50 mg/g, or about 0.3 mg/g to about 40 mg/g). The concentration units are milligrams of enzyme per gram of cellulosic material to be treated.

Processing Steps

In the process of the present invention, cellulosic materials are treated with an extractant, which includes an ionic liquid and a non-solvent. The hemicellulose is dissolved in the extractant, and the resulting extracted hemicellulose is separated from the cellulosic material. The extracted cellulosic material, i.e. cellulose product is recovered for further use. In another embodiment, the extractant is recovered and may be recycled. In another embodiment, the process may further include enzymatic digestion of hemicellulose, extraction and/or isolation of digested hemicellulose and recovery of a cellulosic product with a reduced amount of hemicellulose.

One suitable treatment comprises extracting the cellulosic material with the extractant to selectively dissolve hemicellulose, and thereafter separating the dissolved hemicellulose in the liquid phase from the solid cellulosic product. The solid cellulosic product retains a cellulosic fiber morphology.

In the extraction step, the solid/liquid ratio may range from 0.5/100 to 1/6, depending largely on the extraction apparatus and set-up employed. In batch processes, a solid/liquid ratio of 1.25/100 may be used to facilitate the filtration. In a countercurrent extraction process, a solid/liquid ratio of 1/10 to 1/6 may be used.

In one embodiment, the solid cellulosic product may be washed using a washing agent, e.g., washing solution, which may have the property of dissolving hemicellulose. Therefore, any remaining hemicellulose in the cellulosic product may be dissolved and removed during the washing step.

In one embodiment, the cellulosic product may be subjected to repeat extraction. In one embodiment, the cellulosic product may be treated with the extractant after the initial extraction step to further extract any remaining hemicellulose. In one embodiment, the cellulosic product may be treated with the extractant for a second time after the washing step. In some embodiments, the cellulosic product may be subjected to a third or fourth extraction step.

In one embodiment, the cellulosic material may be subjected to enzyme treatment. In one embodiment, the cellulosic material may be treated with an enzyme after the extraction step. It has now been discovered that more hemicellulose is removed from the cellulosic material when the cellulosic material is first treated with the extractant. Without being bound by theory, by treating the cellulosic material first with the extractant, the enzyme may penetrate the cellulosic material more easily to hydrolyze the hemicellulose. In comparison, less hemicellulose is removed from the cellulosic material when it is first treated with an enzyme followed by extraction.

In one embodiment, after treating with extractant and enzyme, the cellulosic product may be treated with the extractant again to further remove additional hemicellulose.

Washing

In one embodiment, the cellulosic material may be washed using a washing agent to wash and remove hemicellulose and/or enzyme. In one embodiment, the cellulosic material may be washed between extraction treatments. In one embodiment, the cellulosic material may be washed between extraction treatment and enzyme treatment. In one embodiment, the washing agent may be selected from the group consisting of dimethylformamide (DMF), dimethyl sulfoxide (DMSO), N-methyl pyrrolidone, dimethyl acetamide, dimethyl carbonate, propylene carbonate, water, and mixtures thereof.

The treatment of the cellulosic material may be conducted at an elevated temperature, and preferably at atmospheric pressure or slightly above atmospheric pressure. Preferably the contacting is conducted at a temperature from 30° C. to 150° C., e.g., from 50° C. to 130° C., or from 70° C. to 120° C. In terms of upper limit, the treatment of the cellulosic material may be conducted at a temperature of less than 150° C., e.g., less than 130° C., or less than 120° C. In terms of lower limit, the treatment of the cellulosic material may be conducted at a temperature of greater than 30° C., e.g., greater than 50° C., or greater than 70° C. The pressure is in the range from 100 kPa to 150 kPa, preferably from 100 kPa to 120 kPa, more preferably from 100 kPa to 110 kPa.

The cellulosic material may contact the extractant from 5 minutes to 180 minutes, e.g., from 40 minutes to 150 minutes, or from 60 minutes to 90 minutes. In terms of lower limits, the treatment of the cellulosic material may be contacted for at least 5 minutes, e.g., at least 10 minutes or at least 20 minutes. In terms of upper limits, the treatment of the cellulosic material may be contacted for at most 180 minutes, e.g., at most 150 minutes, at most 120 minutes, or at most 60 minutes.

The extraction process may be conducted in a batch, a semi-batch or a continuous process with material flowing either co-current or counter-current in relation to one another. In a continuous process, the cellulosic material contacts the extractant in one or more extraction vessels. In one embodiment, the extractant may be heated to the desired temperature before contacting the cellulosic materials. In one embodiment, the extraction vessel(s) may be heated by any suitable means to the desired temperature.

Counter-Current Extraction

The amount of extractant required has a significant impact on process economics. Counter-current extraction may achieve greater extraction efficiency while maintaining a reasonable extractant usage requirement. Counter-current extraction of solubles from pulp can be accomplished in a variety of commercial equipment such as, but not limited to agitated tanks, hydrapulpers and screw extractors. Twin-screw extractors are generally more efficient than single-screw extractors. Suitable commercial equipment to effect the separation of solid and liquid phases after extraction includes filters, centrifuges, and the like.

Good liquid/solid contact during extraction also depends on the drainage characteristics of the pulp. The particle size of pulp may be important in continuous counter-current extraction because very fine particles tend to compact and cause liquid to channel or block liquid flow completely. Extractant temperature may also have an effect on the extraction of solubles from the pulp.

Rinsing and Drying

The cellulose product may be rinsed using a rinsing agent to remove the extractant, enzyme, dissolved hemicellulose. In one embodiment, the rinsing agent may be selected from the group consisting of water, alcohols, polyols, amino alcohols, aromatic solvents, halogenated solvents, aliphatic solvents, ethers, ketones, esters, formamide, dimethylformamide (DMF), dimethylacetamide, propylene carbonate, dimethyl sulfoxide (DMSO), acetonitrile and mixtures thereof. Specifically, acetone may be use at a last rinsing agent to remove traces of water or other chemicals from the cellulose product.

Cellulose Product

In accordance to the present invention, high purity α-cellulose product is produced. In particular, these high purity α-cellulose products are high purity dissolving grade pulps with less than 5 wt. % hemicellulose. The purity of the α-cellulose may be indicated by a lower absorbance value at a certain wavelength. In one embodiment, for example, the cellulosic product has an absorbance of less than 2.0 at 277 nm, e.g., less than 1.6 at 277 nm, or less than 1.2 at 277 nm. Paper grade pulp, in contrast, typically has an absorbance of greater than 4.7 at 277 nm.

In addition to retaining the fiber morphology of the cellulosic product, the high purity α-cellulose grade pulp product also retains other characteristics such as intrinsic viscosity and brightness. The high purity α-cellulose grade pulp product may be further processed to make cellulose derivatives, such as cellulose ether, cellulose esters, cellulose nitrate, other derivatives of cellulose, or regenerated cellulose fiber, such as viscose, lyocell, rayon, etc. Preferably, the high purity α-cellulose grade pulp may be used to make cellulose acetate.

EXAMPLES Determining Hemicellulose Content Using UV/Vis Example 1

A novel method using UV/Vis analysis method for fast determination of hemicellulose content in a sample was developed. Hemicellulose includes xylan, glucuronoxylan, arabinoxylan, glucomannan, galactomannan, and xyloglucan, while α-cellulose includes glucose. The UV/Vis analysis method was based on the fact that under the pre-hydrolysis conditions xylan degrades to form 2-furfural and glucose degrades to form 5-hydroxymethyl-2-furfural. Because the rate of degradation of the monosaccharide is different, the difference in rate of formation of furfural compounds may be used as the fundamental basis for UV/Vis method.

The UV/Vis analysis method includes a first step of pre-hydrolyzing the sample in sulfuric acid (72 wt. %) for 60±2 min at 30° C. Depending on the concentration of xylan in the sample, 10 ml or 5 ml of deionized water were added to the pre-hydrolysis solution. The solution was then measured at 270 nm to 280 nm with a SHIMADZU UV/Vis spectrometer UV-2600. The final results were adjusted by the dilution factor of the DI water dilution.

Extraction with 1-Ethyl-3-methylimidazoliumacetate (EMIM Ac)/H₂O Extractant Binary System

Example 2

0.5 gram of paper grade pulp sample was weighed and put into a 75 ml glass vial with Teflon face lined cap. A pre-calculated amount of EMIM Ac and H₂O (total) were added into the glass vial according to the predetermined extractant weight ratio (EMIM Ac/H₂O) and mixed well with the pulp samples. The sample thus contained a solid/liquid ratio (S/L) of 1.25:100. The glass vials with pulp and extractant solution were placed into a NAPCO® Autoclave (Model 800-DSE autoclave), and the autoclave was set at 120° C. for 1 hr. After the autoclave treatment, the glass vial was left to cool to room temperature.

The content in the glass vial was transferred to a Buchner funnel with 5 μm twilled Dutch wire cloth filter pads and filtered under vacuum until less than one liquid drop came out of the funnel in a minute. The pulp formed a thin sheet of paper on the pads.

20 ml fresh DMSO solvent was added to the filter pads and were filtered under vacuum again until less than one liquid drop came out of the funnel in a minute. The color of the pad was checked to ensure that the pulp was white without any color. Additional 20 ml of fresh DMSO was added to wash the sample and the sample was placed under vacuum. The process was repeated until the pulp appeared to be white without any color.

Following the DMSO wash, the pulp sheet from the filter pads was dispersed in 40 to 100 ml of water, and then filtered again. This water wash generally was conducted 4 times. 20 ml of acetone was added to the pulp sheet on the filter pads and then a vacuum was applied to dry. The pulp sheet was left dry in a chemical hood overnight.

In some experiments, the extracted pulp samples were subjected to the extraction process again to further improve their purity. In some experiments, instead of the DMSO solvent, the extractant composition (EMIM Ac/H₂O) was used to extract the sample for one or more times. Water was used to wash away the extractant composition.

Example 3

The results for the amount of hemicellulose in the paper pulp product using the above-described EMIM Ac/H₂O binary extractant treatment are shown in Table 1. The absorbance of a commercially available hardwood acetate grade pulp was used as a bench mark. The absorbance of a hardwood paper grade pulp starting material was also measured and used as a comparison.

TABLE 1 EMIM Ac/H₂O Binary Extractant on Hardwood Paper Grade Pulp Extractant Composition by wt. % Absorbance at 277 nm Astracel ECF (Paper Grade Pulp) 4.826 without treatment 30 EMIM Ac/70 H₂O 4.674 40 EMIM Ac/60 H₂O 4.687 50 EMIM Ac/50 H₂O 4.577 60 EMIM Ac/40 H₂O 3.930 70 EMIM Ac/30 H₂O 2.196 80 EMIM Ac/20 H₂O 1.192 90 EMIM Ac/10 H₂O n/a Commercially Available 0.887 Acetate Grade Pulp (Benchmark)

As shown in Table 1, the use of over 50 wt. % water in the EMIM Ac/H₂O binary extractant system appeared to have minimal effect in removing hemicellulose from the hardwood paper grade pulp, while the use of less than 20 wt. % water resulted in the complete dissolution of the paper grade pulp. Surprisingly and unexpectedly, the use of about 20 wt. % water in the EMIM Ac/H₂O binary extractant system removed the greatest amount of hemicellulose without compromising the fiber morphology of the paper grade pulp. The resulting purified pulp product desirably had a very low (1.192) absorbance level. As shown, higher than 80 wt. % EMIM Ac in the extractant resulted in complete dissolution of the hardwood pulp.

Example 4

Table 2 shows the results for the amount of hemicellulose for the treatment of paper grade pulp using EMIM Ac/H₂O binary extractant system on softwood using the procedure of Example 1. The absorbance of a softwood paper grade pulp starting material was also measured and used as a comparison.

TABLE 2 EMIM Ac/H₂O Binary Extractant System on Softwood Paper Grade Pulp Extractant Composition by wt. % Absorbance at 277 nm Paper Grade Pulp 2.05 without treatment 30 EMIM Ac/70 H₂O 2.04 40 EMIM Ac/60 H₂O 2.04 50 EMIM Ac/50 H₂O 1.76 60 EMIM Ac/40 H₂O 1.59 70 EMIM Ac/30 H₂O 1.18 75 EMIM Ac/25 H₂O 0.83 80 EMIM Ac/20 H₂O 0.60 90EMIM Ac/20 H₂O n/a

As shown in Table 2, the use of less than 40 wt. % EMIM Ac in the EMIM Ac/H₂O binary extractant system appeared to have minimal effect in removing hemicellulose from the softwood paper grade pulp. Surprisingly, the use of more than 75 wt. % EMIM Ac in the EMIM Ac/H₂O binary extractant system resulted in a purified paper grade pulp product that had a lower absorbance than samples using less than 75 wt. % EMIM Ac in the EMIM Ac/H2O binary extractant system. The reduction in absorbance at higher level of ionic liquid/water binary systems suggested that more hemicellulose is extracted from the sample at a greater weight percentage of ionic liquid in water. As shown, higher than 80 wt. % EMIM Ac in the extractant resulted in complete dissolution of the softwood pulp.

Example 5

The paper grade pulp fiber morphology was investigated with scanning electron microscopy (SEM). FIG. 1 shows the SEM micrograph for a starting material hardwood paper grade pulp and FIG. 2 shows the SEM micrograph for a starting material softwood paper grade pulp. The fiber morphology of the hardwood pulp and softwood pulp are observed in these SEM micrographs. The starting material paper grade pulps were treated with the methods of the instant invention. FIGS. 3 and 4 show SEM micrographs for the hardwood paper grade pulp and the softwood paper grade pulp after the treatment, respectively. As shown in FIGS. 3 and 4, the wood fiber morphology for both hardwood and softwood remains intact, although some small pores were observed due to the selective removal of hemicellulose from the fiber structure. This porous fiber morphology is advantageous for downstream cellulose derivatization such as acetylation, etherification, or nitration by providing additional physical access route to chemical reagents. FIGS. 5 and 6 show SEM micrographs for the hardwood paper grade pulp and the softwood paper grade pulp, respectively, treated using an ionic liquid and regenerated using a non-solvent. As shown in both figures, the fiber morphology of the cellulosic structure is destroyed. The figures demonstrate the benefits of using the solvent systems of the present invention to obtain high purity α-cellulose and retaining its fiber morphology.

Example 6

In addition to paper grade pulp, experiments were also conducted using viscose pulp. Table 3 compares two different viscose pulps and the treatment of which using the 75 wt. % EMIM Ac/25 wt. % H₂O binary extractant system.

TABLE 3 75 wt. % EMIM Ac/25 wt. % H₂O Binary Extractant System Treatment of Viscose Pulp Absorbance at 277 nm Untreated Treated Commercial Viscose I 1.11 0.69 Commercial Viscose II 0.93 0.66 Commercially 0.79 — Available Hardwood Acetate Pulp (Control)

Table 3 shows that in addition to using paper grade pulp as starting material, the present invention may also use other starting materials, such as viscose pulp. Commercial viscose pulps by two different manufacturers were treated using the EMIM Ac/H₂O binary extractant system. The data showed that by treating the viscose pulp with a binary extractant system of 75 wt. % EMIM Ac/25 wt. % H₂O, the treated pulp product had less hemicellulose than the commercially available acetate grade pulp. The invention is accordingly applicable to other pulp starting materials in addition to paper grade pulp, such as viscose grade pulp, fluff grade pulp, or acetate grade pulp for extremely high purity applications.

Example 7

Samples of hardwood paper grade pulp were subjected to repeated EMIM Ac/H₂O treatment using 75 wt. %/25 wt. % EMIM Ac/H₂O and 70 wt. %/30 wt. % EMIM Ac/H₂O. The amount of hemicellulose in the samples was measured using the procedure in Example 1 and is shown in Table 4.

TABLE 4 EMIM Ac/H₂O Repeat Binary Extractant System Treatment Absorbance at 277 nm EMIM Ac/H₂O 1^(st) Treatment 2^(nd) Treatment 75 wt. %/25 wt. % 1.509 1.049 70 wt. %/30 wt. % 1.636 1.351

As shown in Table 4, more hemicellulose was extracted during the second EMIM Ac/H₂O treatment. This treatment resulted in the lower absorbance values of the paper pulp product at 277 nm. Therefore, repeated treatment of the paper grade pulp in this binary system increased the purity of the paper pulp product by removing more hemicellulose.

Extraction with 1-Ethyl-3-methylimidazoliumacetate (EMIM Ac)/DMSO Extractant Binary System

Example 8

0.5 gram of paper grade pulp sample was weighed and put into a 75 ml glass vial with Teflon face lined cap. A pre-calculated amount of EMIM Ac and DMSO (total) were added into the glass vial according to the predetermined extractant weight ratio (EMIM Ac/DMSO) and mixed well with the pulp samples. The sample thus contained a solid/liquid ratio (S/L) of 1.25:100. The glass vials with pulp and extractant solution were placed into a NAPCO® Autoclave (Model 800-DSE autoclave), and the autoclave was set at 120° C. for 1 hr. After the autoclave treatment, the glass vial was left to cool to room temperature.

The content in the glass vial was transferred to a Buchner funnel with 5 μm twilled Dutch wire cloth filter pads and filtered under vacuum until less than one liquid drop came out of the funnel in a minute. The pulp formed a thin sheet of paper on the pads.

20 ml fresh DMSO solvent were added to the filter pads and were filtered under vacuum again until less than one liquid drop came out of the funnel in a minute. The color of the pad was checked to ensure that the pulp was white without any color. An additional 20 ml of fresh DMSO was added to wash the sample and the sample was placed under vacuum. The process was repeated until the pulp appeared to be without any color.

Following the DMSO wash, the pulp sheet from the filter pads was dispersed in 40 to 100 ml of water, and then filtered again. This water wash generally was conducted 4 times. 20 ml of acetone was added to the pulp sheet on the filter pads followed by application of vacuum to dryness. The pulp sheet was left dry in chemical hood overnight.

In some experiments, the extracted pulp samples were subjected to the extraction process again to further improve its purity. In some experiments, instead of the DMSO solvent, the extractant composition (EMIM Ac/DMSO) was used to extract the sample for one or more times. Water was used to wash away the extractant composition.

Example 9

Table 5 shows the results for the amount of hemicellulose for the treatment of paper grade pulp using EMIM Ac/DMSO binary extractant system on hardwood using the procedure of Example 8. The absorbance of a hardwood paper grade pulp starting material was also measured and used as a comparison.

TABLE 5 EMIM Ac/DMSO Binary Extractant on Hardwood Paper Grade Pulp Extractant Composition by wt. % Absorbance at 277 nm Hardwood Paper Grade Pulp 4.826 without treatment 100 DMSO 4.674 1 EMIM Ac/99 DMSO 1.93 2.5 EMIM Ac/97.5 DMSO 0.89 5 EMIM Ac/95 DMSO 0.88 8 EMIM Ac/92 DMSO cellulose dissolution occurs Commercially Available 0.89 Acetate Grade Pulp (Benchmark)

As shown in Table 5, the use of DMSO as a non-solvent with EMIM Ac beneficially reduced the amount of EMIM Ac necessary for purifying paper grade pulp. The use of DMSO alone appeared to have minimal effect in removing hemicellulose from the hardwood paper grade pulp. Surprisingly, the use of more than 1 wt. % EMIM Ac in the EMIM Ac/DMSO binary extractant system resulted in a purified paper grade pulp product that had significantly lower absorbance of 1.93 at 277 nm. In particular, the use of 2.5-5 wt. % EMIM Ac in the EMIM Ac/DMSO binary extractant system yielded products that have similar purity to commercially available acetate grade pulp. However, the use of more than 8 wt. % EMIM Ac in the binary extractant system resulted in the complete dissolution of the pulp. This result suggests that by using an appropriate mixture of EMIM Ac and non-solvent DMSO, a maximum amount of hemicellulose may be removed from the hardwood paper grade pulp.

Example 10

Table 6 shows the results for the amount of hemicellulose for the treatment of paper grade pulp using EMIM Ac/DMSO binary extractant system on softwood using the procedure of Example 8. The absorbance of a softwood paper grade pulp starting material was also measured and used as a comparison.

TABLE 6 EMIM Ac/DMSO Binary Extractant on Softwood Paper Grade Pulp Extractant Composition by wt. % Absorbance at 277 nm Softwood Paper Grade Pulp 1.75 without treatment 1 EMIM Ac/99 DMSO 1.48 2.5 EMIM Ac/97.5 DMSO 1.07 8 EMIM Ac/92 DMSO cellulose dissolution

As shown in table 7, the use of 1 wt. % EMIM Ac/99 wt. % DMSO beneficially reduced the absorbance from 1.75 to 1.48 at 277 nm. In comparison, 8 wt % EMIM Ac/92 wt. % DMSO completely dissolved the softwood paper grade pulp. Surprisingly, the use of 2.5 wt. % EMIM Ac in the EMIM Ac/DMSO binary extractant system beneficially reduced the absorbance to 1.07 at 277 nm. This result suggests that by using an appropriate mixture of EMIM Ac and non-solvent DMSO, a maximum amount of hemicellulose may be removed from the softwood paper grade pulp.

Extraction with EMIM Ac/H₂O/DMSO Tertiary Extractant System Example 11

0.5 gram of paper grade pulp sample was weighed and put into a 75 ml glass vial with Teflon face lined cap. EMIM Ac/H2O (75/25 wt. %/wt. %) and DMSO were added into the glass vial according to the predetermined extractant weight ratio and mixed well with pulp samples. This provided a solid/liquid ratio (S/L) 1.25:100. The glass vials with pulp and extractant solution were placed into a NAPCO® Autoclave (Model 800-DSE autoclave), and the autoclave was set at 120° C. for 1 hr. After the autoclave treatment, the glass vial was left to cool to room temperature.

The content in the glass vial was transferred to a Buchner funnel with 5 μm twilled Dutch wire cloth filter pads and filtered under vacuum until less than one liquid drop came out of the funnel in a minute. The pulp formed a thin sheet of paper on the pads.

The filter pads were added 20 ml fresh DMSO solvent and then filtered under vacuum again until less than one liquid drop came out of the funnel in a minute. The color of the pad was checked to ensure that the pulp was white without any color. An additional 20 ml of fresh DMSO was added to wash the sample and the sample was placed under vacuum. The process was repeated until the pulp appeared to be without any color.

Following DMSO wash, the pulp sheet from the filter pads was dispersed in 40 to 100 ml of water, and then filtered again. This water wash was generally conducted 4 times. Then 20 ml of acetone was added to the pulp sheet on the filter pads and vacuum was applied to dryness. The pulp sheet was left to dry overnight in a chemical hood.

In some experiments, the extracted pulp samples were subjected to the extraction process again to further improve their purity. In some experiments, instead of the DMSO solvent, the extractant composition (EMIM Ac/H₂O) was used to extract the sample one or more times. Water was used to wash away the extractant composition.

Example 12

The results for the amount of hemicellulose in the paper pulp product using the above-described EMIM Ac/H2O/DMSO tertiary extractant system are shown in Table 7. The absorbance of commercially available acetate grade pulp and the starting material paper grade pulp, are provided as references.

TABLE 7 EMIM Ac/H₂O/DMSO Tertiary Extractant System Treatment on Hardwood Paper Grade Pulp Extractant Composition by wt. % Absorbance at 277 nm Commercially Available 0.737 Acetate Grade Pulp Paper Grade Pulp 4.862 (without treatment) 100 [75 EMIM Ac/25 H₂O]/0 DMSO 2.131 50 [75 EMIM Ac/25 H₂O]/50 DMSO 0.873 37.5 [75 EMIM Ac/25 H₂O]/62.5 DMSO 0.745 25 [75 EMIM Ac/25 H₂O]/75 DMSO 0.715 12.5 [75 EMIM Ac/25 H₂O]/87.5 DMSO 0.737 2.5 [75 EMIM Ac/25 H₂O]/97.5 DMSO 1.328

The extractant compositions used in Table 7 are 75 wt. % EMIM Ac/25 wt. % H₂O combined with different weight percentages of DMSO. This example illustrates the effect of DMSO in the extractant system. As shown in Table 5, by using 0 wt. % DMSO, the absorbance of the sample dropped from 4.862 to 2.131. However, more hemicellulose was removed with the use of DMSO. Surprisingly and unexpectedly, the use of 75 wt. % DMSO in combination with 25% of a mixture containing 75 wt. % EMIM Ac/25 wt. % H₂O resulted in a pulp product that had a lower absorbance level than the commercially available acetate grade pulp. Furthermore, the use of a system with 87.5 wt. % DMSO resulted in a pulp product having the same purity as the commercially available acetate grade pulp. Given the high cost of ionic liquids, e.g., EMIM Ac, the use of DMSO in the extractant system beneficially reduced the cost of the purification of paper grade pulp to make acetate grade pulp.

Example 13

Samples of hardwood paper grade pulp were subjected to repeated EMIM Ac/H₂O/DMSO treatment using 50 wt. % [75 wt. % EMIM Ac/25 wt. % H₂O]/50 wt. % DMSO and 50 wt. % [70 wt. % EMIM Ac/30 wt. % H₂O]/50 wt. % DMSO. The amount of hemicellulose in the samples was measured using the procedure in Example 1 and is shown in Table 8.

TABLE 8 EMIM Ac/H₂O/DMSO Repeat Tertiary Extractant System Treatment Absorbance at 277 nm EMIM Ac/H₂O/DMSO 1^(st) Treatment 2^(nd) Treatment 50 [75 EMIM Ac/25 H₂O]/50 DMSO 0.791 0.677 50 [70 EMIM Ac/30 H₂O]/50 DMSO 1.165 1.150

As shown in Table 8, more hemicellulose was extracted during the second EMIM Ac/H₂O/DMSO treatment. This treatment resulted in the lower absorbance values of the paper pulp product at 277 nm. The repeated treatment of the paper pulp using 50 wt. %[75 wt. % EMIM Ac/25 wt. % H₂O]/50 wt. % DMSO resulted in a pulp product having 0.677 absorbance, which is lower than the commercially available acetate grade pulp. Therefore, repeated treatments of the paper grade pulp in this tertiary system increased the purity of the paper pulp product by removing more hemicellulose.

Enzyme Treatment Example 14

Unless noted otherwise, hydrolysis was carried out for 4 hours at 40° C., pH 4.8, and a volume of 12.5 μL of the commerical Pulpzyme® enzyme solution for 0.5 g or pulp at a concentration of 60 mg/mL of pulp, with mixing at 900 rpm. Sugar was detected with the standard DNS assay and the pulp purity was monitored with UV/Vis test method described above.

Example 15

Samples of hardwood paper pulp were subjected to enzyme treatment using Pulpzyme and EMIM Ac/H₂O treatment (25 wt. % EMIM Ac/75 wt. % H₂O). The amount of hemicellulose in the samples was measured using the procedure in Example 1 and is shown in Table 9.

TABLE 9 EMIM Ac/H₂O Binary Extractant System Treatment and Enzyme Treatment on Hardwood Paper Grade Pulp Samples Absorbance @ 277 nm Paper Grade Pulp 4.86 without treatment Pulpzyme Treatment 4.34 EMIM Ac/H₂O Treatment 1.73 EMIM Ac/H₂O Treatment followed 1.54 by Pulpzyme Treatment EMIM Ac/H₂O Treatment followed 1.35 by Pulpzyme Treatment then EMIM Ac/H₂O Treatment Commercially Available Acetate 0.79 Grade Pulp

As shown in Table 9, the use of enzyme alone removed some hemicellulose from the paper grade pulp. The absorbance was reduced from 4.86 to 4.34. In comparison, the use of the extractant system according to the invention significantly reduced the absorbance from 4.86 to 1.73. By treating the paper grade pulp with the extractant system followed by enzyme treatment, additional hemicellulose was removed and the absorbance was further reduced from 1.73 to 1.54. The paper grade pulp may be treated with the extractant system again after an initial extractant system and enzyme treatment. This repeated treatment resulted in the reduction of absorbance from 1.54 to 1.35.

Example 16

A multi-stage extraction was performed in order to simulate counter-current extraction. All extraction operations were carried out for 1 hour in a bath heated to 95° C.±2° C. Both 2.5 wt. % EMIM Ac in DMSO and 2.0 wt. % EMIM Ac in DMSO solutions were evaluated as the extractants. After 1 hour of extraction, the reaction mixture was cooled to room temperature and centrifuged in an MR23i Centrifuge from Thermo Scientific to separate the extraction solvents (filtrate) and the pulp. Both pulps and extraction solvents were then recycled, to obtain the representative final pulp and extraction solvent.

In particular, a first extraction was performed solely to obtain a filtrate, to be used in a second extraction. Thus, following a first extraction of 0.2 grams of Pulp A and 16 grams of fresh solvent, the reaction mixture was centrifuged to provide Filtrate 1A. Pulp A′, the other product of the first extraction, was discarded because, as noted above, the first extraction was performed solely to obtain Filtrate 1A. Following the second extraction of 0.2 grams of Pulp B (from the same batch as Pulp A) and 16 grams of Filtrate 1A from the first extraction, the reaction mixture was centrifuged to provide Pulp B′, to be used in a third extraction. Filtrate 2B, the other product of the second extraction, was discarded as representing the filtrate coming out of the counter-current extraction before the process reached steady state. Following the third extraction of 0.2 grams of Pulp B′ (from the second extraction) and 16 grams of fresh solvent, the reaction mixture was centrifuged to provide Pulp B″, which represented the final pulp.

Filtrate 3B, the other product of the third extraction, in an amount of 16 grams, was then used in a fourth extraction of 0.2 grams of Pulp C (from the same batch as Pulp A and B), and the reaction mixture was centrifuged to provide Filtrate 4C, which represented the final extractant. Pulp C′, the other product of the fourth extraction, was discarded as representing pulp coming out of the counter-current extraction before the process reaches steady state.

The UV-Vis purity of the pulp and comparative direct extraction (i.e., single extraction for 1 hour in a bath heated to 95° C.±2° C., followed by cooling to room temperature and centrifugation in an MR23i Centrifuge from Thermo Scientific to separate the filtrate and the pulp) results are summarized in Tables 10, 11, and 12, below.

TABLE 10 Comparative UV-Vis results of purified pulp (S/L = 1.25%, 2.5% EMIM Ac/DMSO) UV Absorbance @ 278 nm Direct Extraction Multi-Stage Extraction Sample S/L = 1.25%, 2.5% EMIM Ac S/L = 1.25%, 2.5% EMIM Ac 1 1.01 0.87 2 0.99 0.85 3 0.93 0.90 4 1.01 0.87 Average 0.99 0.87

TABLE 11 Comparative UV-Vis results of purified pulp (S/L = 2.5%, 2.5% EMIM Ac/DMSO) UV Absorbance @ 278 nm Direct Extraction Multi-Stage Extraction Sample S/L = 2.5%, 2.5% EMIM Ac S/L = 2.5%, 2.5% EMIM Ac 1 1.274 1.156 2 1.377 1.328 3 1.314 1.269 Average 1.321 1.251

TABLE 12 Comparative UV-Vis results of purified pulp (S/L = 1.25%, 2.0% EMIM Ac/DMSO) UV Absorbance @ 278 nm Direct Extraction Multi-Stage Extraction Sample S/L = 1.25%, 2.0% EMIM Ac S/L = 1.25%, 2.0% EMIM Ac 1 1.26 1.25 2 1.24 1.26 Average 1.25 1.26

Based on the results from Tables 10 and 11, the UV-Vis absorbance of the purified pulp from 2.5 wt. % EMIM Ac in DMSO was reduced (i.e., from 0.99 to 0.87 for S/L=1.25% and from 1.32 to 1.25 for S/L=2.5%) by multi-stage extraction versus direct extraction, indicating that counter extraction increased extraction efficiency. Based on the results from Table 12, the UV-Vis absorbance of the purified pulp from 2.0 wt. % EMIM Ac in DMSO for S/L=1.25% shows no difference between multi-stage extraction and direct extraction, which suggests that extraction efficiency may depend on extractant solvation power to hemicellulose.

Thus, without being bound by theory, when the extractant has high solvation power to hemicellulose, counter-current extraction could make full use of that extraction power to reduce the hemicellulose in the pulp and thus improve extraction efficiency.

While the invention has been described in detail, modifications within the spirit and scope of the invention will be readily apparent to those of skill in the art. It should be understood that aspects of the invention and portions of various embodiments and various features recited above and/or in the appended claims may be combined or interchanged either in whole or in part. In the foregoing descriptions of the various embodiments, those embodiments which refer to another embodiment may be appropriately combined with other embodiments as will be appreciated by one of ordinary skill in the art. Furthermore, those of ordinary skill in the art will appreciate that the foregoing description is by way of example only, and is not intended to limit the invention. 

We claim:
 1. A solvent system for selectively reducing hemicellulose in a cellulosic material to form a hemicellulose reduced cellulosic product, comprising at least 0.1 wt. % ionic liquid and at least 5 wt. % non-solvent.
 2. The solvent system of claim 1, comprising from 0.1 to 95 wt. % ionic liquid and from 5 to 99.5 wt. % non-solvent.
 3. The solvent system of claim 1, wherein the ionic liquid is selected from the group consisting of 1-butyl-3-methyl imidazolium tetrachloroaluminate, 1-ethyl-3-methyl imidazolium tetrachloroaluminate, 1-ethyl-3-methyl imidalzolium hydrogensulfate, 1-butyl-3-methyl imidazolium hydrogensulfate, methylimidazolium chloride, 1-ethyl-3-methyl imidazolium acetate, 1-butyl-3-methyl imidazolium acetate, tris-2(hydroxyl ethyl)methylammonium methylsulfate, 1-ethyl-3-methyl imidazolium ethylsulfate, 1-ethyl-3-methyl imidazolium methanesulfonate, methyl-tri-n-butylammonium methylsulfate, 1-butyl-3-methyl imidazolium chloride, 1-ethyl-3-methyl imidasolium chloride, 1-ethyl-3-methyl imidazolium thiocyanate, 1-butyl-3-methyl imidazolium thiocyanate, 1-aryl-3-methyl imidazolium chloride, and mixtures and complexes thereof.
 4. The solvent system of claim 1, wherein the ionic liquid is 1-ethyl-3-methyl imidazolium acetate.
 5. The solvent system of claim 1, wherein the non-solvent is selected from the group consisting of water, alcohols, n-butanol, tert-butanol, diols, polyols, amino alcohols, aromatic solvents, halogenated solvents, aliphatic solvents, ethers, ketones esters, amides, and mixtures thereof.
 6. The solvent system of claim 1, wherein the non-solvent is selected from the group consisting of water, methanol, ethanol, n-propanol, isopropanol, n-butanol, tert-butanol, ethanediol, propanediol, ethanolamine, diethanolamine, triethanolamine, benzene, toluene, ethylbenzene, xylene, dichloromethane, chloroform, carbon tetrachloride, dichloroethane, chlorobenzene, pentane, hexane, heptane, octane, ligroin, petroleum ether, cyclohexane, decalin, tetrahydrofuran, diethyl ether, methyl tert-butyl ether, diethylene glycol monomethyl ether, acetone, methyl ethyl ketone, ethyl acetate, dimethyl carbonate, dipropyl carbonate, propylene carbonate, formamide, dimethylformamide, dimethylacetamide, dimethyl sulfoxide, acetonitrile and mixtures thereof.
 7. The solvent system of claim 1, wherein the non-solvent is acetonitrile.
 8. The solvent system of claim 1, wherein the non-solvent is dimethyl sulfoxide.
 9. The solvent system of claim 1, wherein the non-solvent comprises water and an organic non-solvent.
 10. The solvent system of claim 9, wherein the solvent system comprises from 0.1 to 50 wt. % ionic liquid and from 0.5 to 18 wt. % water.
 11. The solvent system of claim 1, wherein the non-solvent is an organic non-solvent and wherein the solvent system comprises from 92.1 to 99.9 wt. % organic non-solvent and from 0.1 to 7.9 wt. % ionic liquid.
 12. The solvent system of claim 1, wherein the solvent system comprises a first non-solvent and a second non-solvent, and further wherein the solvent system comprises from 10 to 98 wt. % second non-solvent.
 13. The solvent system of claim 1, wherein the solvent system comprises a first non-solvent and a second non-solvent, and further wherein the second non-solvent decreases the viscosity of the solvent system.
 14. A solvent system for selectively reducing hemicellulose in a cellulosic material to form a hemicellulose reduced cellulosic product, comprising 50-80 wt. % ionic liquid and 20-50 wt. % water.
 15. The solvent system of claim 14, further comprising dimethyl sulfoxide, dimethylformamide, methanol, ethanol, isopropanol, acetone, acetic acid or a mixture thereof.
 16. The solvent system of claim 14, wherein the ionic liquid is selected from the group consisting of 1-butyl-3-methyl imidazolium tetrachloroaluminate, 1-ethyl-3-methyl imidazolium tetrachloroaluminate, 1-ethyl-3-methyl imidalzolium hydrogensulfate, 1-butyl-3-methyl imidazolium hydrogensulfate, methylimidazolium chloride, 1-ethyl-3-methyl imidazolium acetate, 1-butyl-3-methyl imidazolium acetate, tris-2(hydroxyl ethyl)methylammonium methylsulfate, 1-ethyl-3-methyl imidazolium ethylsulfate, 1-ethyl-3-methyl imidazolium methanesulfonate, methyl-tri-n-butylammonium methylsulfate, 1-butyl-3-methyl imidazolium chloride, 1-ethyl-3-methyl imidasolium chloride, 1-ethyl-3-methyl imidazolium thiocyanate, 1-butyl-3-methyl imidazolium thiocyanate, 1-aryl-3-methyl imidazolium chloride, and mixtures and complexes thereof.
 17. The solvent system of claim 14, wherein the ionic liquid is 1-ethyl-3-methyl imidazolium acetate.
 18. The solvent system of claim 14, further comprising acetonitrile.
 19. A solvent system for selectively reducing hemicellulose in a cellulosic material to form a hemicellulose reduced cellulosic product, comprising at most 50 wt. % ionic liquid, at most 18 wt. % water, and at least 10 wt. % dimethyl sulfoxide.
 20. The solvent system of claim 19, wherein the ionic liquid is selected from the group consisting of 1-butyl-3-methyl imidazolium tetrachloroaluminate, 1-ethyl-3-methyl imidazolium tetrachloroaluminate, 1-ethyl-3-methyl imidalzolium hydrogensulfate, 1-butyl-3-methyl imidazolium hydrogensulfate, methylimidazolium chloride, 1-ethyl-3-methyl imidazolium acetate, 1-butyl-3-methyl imidazolium acetate, tris-2(hydroxyl ethyl)methylammonium methylsulfate, 1-ethyl-3-methyl imidazolium ethylsulfate, 1-ethyl-3-methyl imidazolium methanesulfonate, methyl-tri-n-butylammonium methylsulfate, 1-butyl-3-methyl imidazolium chloride, 1-ethyl-3-methyl imidasolium chloride, 1-ethyl-3-methyl imidazolium thiocyanate, 1-butyl-3-methyl imidazolium thiocyanate, 1-aryl-3-methyl imidazolium chloride, and mixtures and complexes thereof. 